29/10/2019 Production methodology Langmuir (2005) 21 , 6572 - 6575 - PDF document

29/10/2019 Production methodology Langmuir (2005) 21 , 6572 - 6575 Poly(1-methylpyrrol-2-ylsquaraine) Hollow silica shells PMPS particles Core shell products PMPS particles 1 29/10/2019 PMPS particle parameters particle size: 1.3 2


  1. 29/10/2019 Production methodology Langmuir (2005) 21 , 6572 - 6575 Poly(1-methylpyrrol-2-ylsquaraine) Hollow silica shells PMPS particles Core shell products PMPS particles 1

  2. 29/10/2019 PMPS particle parameters • particle size: 1.3 – 2 μm diameter • few beads with diameters up to 4 μm • thermally stable up to 280ºC • mean nominal stress at rupture: 493  113 MPa • mean deformation at rupture: + 65% initial diameter • polymer additives / functional fillers • storage and slow release • separation / filtration media TGA data 100 90 o 300 C 80 30 mins Weight Loss (%) 70 60 50 o 10 C / min 40 440 C o 30 20 10 0 0 100 200 300 400 500 600 700 Temperature ( o C) 2

  3. 29/10/2019 Absorbent sponges Plastics additives Porosity 3

  4. 29/10/2019 Porosity Uranium Chlorine Uranium Porosity Chlorine – light blue Uranium - red 4

  5. 29/10/2019 Hollow silica shells Silica shell parameters • particle size: 650 nm – 1.0 μm diameter • wall thickness ≥10% diameter • aggregated • mean nominal stress at rupture: XRD pattern 438  47 MPa • mean deformation at rupture: + 53% initial diameter 30 60 90 • BET SSA > 370 m 2 /g Degrees 2  5

  6. 29/10/2019 Silica shell parameters Encapsulated metals - M n+ @SiO 2 6

  7. 29/10/2019 Encapsulated dyes and pigments Organic dyes@SiO 2 YVO 4 -Eu 2% @SiO 2 Principal applications • Storage and controlled release media • Slow release media • Encapsulated optical media (i.e. dyes, pigments etc.) • Encapsulated fragrances and flavours • Encapsulated UV absorbents • Polymer additives / Functional fillers • Biological / catalysis support media • Separation / filtration media 7