material development in lead bismuth spallation target
play

MATERIAL DEVELOPMENT IN LEAD BISMUTH SPALLATION TARGET SYSTEM - PowerPoint PPT Presentation

MATERIAL DEVELOPMENT IN LEAD BISMUTH SPALLATION TARGET SYSTEM Kenji KIKUCHI, Shigeru SAITO, Dai HAMAGUCHI, Masao TEZUKA, Hironari OBAYASHI / J-PARC Center Practice Prospect 10 th OECD NEA Meeting on AFPP and T, Mito, 2008 Liq. He ADS RF


  1. MATERIAL DEVELOPMENT IN LEAD BISMUTH SPALLATION TARGET SYSTEM Kenji KIKUCHI, Shigeru SAITO, Dai HAMAGUCHI, Masao TEZUKA, Hironari OBAYASHI / J-PARC Center Practice Prospect 10 th OECD NEA Meeting on AFPP and T, Mito, 2008

  2. Liq. He ADS RF Injector Beam duct RFQ DTL Superconducting linac P Beam Beam window window MA PbBi (Am,Cm) n Reactor MA The Achilles’ tendon is a PbBi beam window in ADS. We will replace every ?-year. 10 th OECD NEA Meeting on AFPP and T, Mito, 2008

  3. Transmutation Experimental Facility (TEF) Transmutation Physics Experimental Facility : TEF-P ADS Target Test Facility : TEF-T 10W Critical Assembly 200kW Pb-Bi Target Shield Laser Charge Exchange 10 th OECD NEA Meeting on AFPP and T, Mito, 2008

  4. ADS Target test facility • LBE spallation target test had planned in J-PARC phase II program. • LBE controlling techniques acquisition was a goal of R&Ds. • LBE loops were run for corrosion-erosion (JLBL-1), target model (JLBL-2) and thermal fluid (JLBL-3) • Proton irradiation depended on SINQ at PSI(STIP & MEGAPIE). 10 th OECD NEA Meeting on AFPP and T, Mito, 2008

  5. Lead Bismuth Loop - 1 for corrosion JLBL-1 JLBL-1 10 th OECD NEA Meeting on AFPP and T, Mito, 2008

  6. Production of PbO Production of PbO RTlnP O 2 O 4 3 O Dissolution of Fe 3 Dissolution of Fe 4 Temperature 10 th OECD NEA Meeting on AFPP and T, Mito, 2008

  7. Y LBE Velocity Zero Vo X 10 th OECD NEA Meeting on AFPP and T, Mito, 2008

  8. JLBL-2 10 th OECD NEA Meeting on AFPP and T, Mito, 2008

  9. 10 th OECD NEA Meeting on AFPP and T, Mito, 2008

  10. JLBL-3 10 th OECD NEA Meeting on AFPP and T, Mito, 2008

  11. 10 th OECD NEA Meeting on AFPP and T, Mito, 2008

  12. K HAYASHI, et. al, AESJ, 7-1, 2008,P44-57. 10 th OECD NEA Meeting on AFPP and T, Mito, 2008

  13. STIP 10 th OECD NEA Meeting on AFPP and T, Mito, 2008

  14. RT 250℃ 10 th OECD NEA Meeting on AFPP and T, Mito, 2008

  15. S SAITO, et. al, JNM, 343, 2005,P253-261.

  16. 100 µ m 100 µ m Fig. 11. Fracture surface of tensile Fig. 12. Fracture surface of specimen irradiated to 10.1 dpa tensile specimen irradiated to and tested at RT . 10.1 dpa and tested at 250 o C . K KIKUCHI, et. al, AccApp03, 2003.

  17. Corrosion in another loop 450℃×3000h 10 th OECD NEA Meeting on AFPP and T, Mito, 2008

  18. F82H<500C JPCA<450C 4 5 0 ℃ × 4 5 0 ℃ × 450℃×1000h 450℃×1000h 1000h 1000h 10 µ m 10 µ m 450℃×3000h 4 5 0 ℃ × 4 5 0 ℃ × 3000h 3000h 500℃×1000h 500℃×1000h 5 0 0 ℃ × 5 0 0 ℃ × 1000h 1000h K KIKUCHI, et. al, JNM, 377, 2008,P232-242 10 th OECD NEA Meeting on AFPP and T, Mito, 2008

  19. Achievements of our Practice • Proton irradiation Data base for austenitic steel have been obtained up to 20 dpa, which included mechanical property and micro-nano structure. • JLBL-1 Materials property under LBE flow was obtained through 18000 hrs run. Oxygen sensor property and performance of EMP were investigated. • JLBL-2 EMP drove LBE in the coaxial counter flows. EMF performance was investigated. Ultrasonic Doppler prove visualized LBE flow. • JLBL-3 Massive flow control was experienced (500L/min). Heat transfer coefficient of the beam model was formulized. 10 th OECD NEA Meeting on AFPP and T, Mito, 2008